Terrible pic related. Can i harden a flat, front surface with an induction heater? Instead of putting the induction coil around an object, in this case a simplified pipe, i'd put the induction heater straight in front, similar to an induction stove. Basically i don't have a fancy oven, but a fancy induction heater can be had for 20€ a day here. Unfortunately every example online seems to be about welding and, or putting the induction coil around your object, not in front.
>>3004838One with a pancake coil is probably what you would want. Site related:https://www.uihm.com/english/induction-heating-steel-plate-surface-by-pancake-induction-co-2-80-2553.html
>>3004838I have one of those induction heaters. the duty cycle is too short for anything more than 5 or 10mm.
>>3004849Hell yeah, that's exactly what i need.
>>3004838Yes you can, flat coils exist and this is actually part of a common hardening depth testing procedure. >Induction heater for rentIn general if it's a serious pieve of kit you should be fine putting any load or even a short on the output as pong as it's bot capacitive. But I'd ask if they have a flat coil or allow you to put custom coils on before doing to. Making a primitive induction heater is cheap and easy.
>>3004838>i'd put the induction heater straight in front, similar to an induction stoveIt would depend on the strength of the field where it intersects your metal object and the heat you are aiming for. I would doubt this will work. What would work is if you put the rod into the coil, just enough to to fill the coil, and heat part of the rod and the tip at the same time.
>>3004867Been thinking a bit more. OP, you can always use various means to redirect a magnetic field as you see fit if your situation is that you can rent the machine but not change the coil. Ferrite core material can do it but even more so you can simply wind a pickup coil and work coil and close the loop. It would ha e the additional advantage of providing some loose coupling between the two coils. In my experience especially self oscillating heaters can crash if coupling to the work is too good.
>>3004838Is your pipe made of heat treatable steel? What precisely are you wanting to make?What makes a hardened pipe the optimal way to get what you want?
>>3006696Yes and fuck off.
>>3004838Torch hardening was doing that task long before electric induction heaters proliferated. It's a common student exerciseto torch harden then inspect with a Rockwell tester to ensure it was done correctly. Some of the best hardening and tempering info for home gamers is in muzzleloading forums with useful small examples like frizzens.